White Magic E-43 – Acrylic Gauntlet Impregnation Binder
Value-tier grade in the GT range for cost-sensitive gauntlet production
Part of the White Magic range by Focus Polymers
White Magic E-43 is a self-crosslinked acrylic copolymer emulsion engineered for polyester tubular gauntlet fabric used in lead-acid battery separators. It is the economical grade in the GT range, formulated for cost-sensitive applications without compromising core stiffening performance.
Grade Positioning
E-43 is our value-tier grade, recommended where cost efficiency is the primary consideration.
Key Performance Attributes
High stiffness imparts the structural rigidity required for tubular battery gauntlets — the cured film is intentionally stiff and brittle. Self-crosslinking chemistry means no external crosslinker is required. E-43 offers excellent acid resistance in sulphuric acid electrolyte, oxidation resistance for long-term durability inside lead-acid batteries, high thermal stability up to 215°C curing temperature, and controlled porosity that allows electrolyte flow while retaining active material. Stiffness and oxidation resistance vary by grade across the GT range — contact us for comparative test data for your application.
Method of Application
Step 1 — Impregnation: dip 100% PET woven tubular gauntlet fabric into E-43 emulsion, adjusting weight pick-up to 25–30% via padding rolls to achieve target stiffness. Step 2 — Drying: dry impregnated fabric at 70°C for 30 minutes. Step 3 — Cutting & Rodding: cut fabric to required dimensions and insert stainless steel rods into the gauntlet tubes. Step 4 — Curing: cure at 200–215°C for 10 minutes to activate crosslinking. Step 5 — Finishing: de-rod and pack.
Shelf Life & Storage
Four months in the original sealed container. Store in a cool, dry, shaded place at 5°C to 35°C. Protect from freezing. Available in 55 kg and 220 kg pack sizes.
Specifications
| Parameter | Value |
|---|---|
| Appearance | Milky white emulsion |
| Chemistry | Self-crosslinking acrylic copolymer |
| Solids Content (105°C, 3 hrs) | 43 ± 1% |
| pH @ 30°C | 6 – 7 |
| Viscosity, Brookfield (RVT #2/20/30°C) | 80 – 120 cps |
| Viscosity, Flow Cup (B4 Ford Cup, 30°C) | 14 – 18 seconds |
| Curing Temperature | 200 – 215°C for 10 minutes |
| Shelf Life | 4 months in sealed container |
| Storage Temperature | 5°C – 35°C, protect from freezing |
| Packing | 55 kg and 220 kg |
Applications
- •Stiffening binder for PET tubular gauntlet in lead-acid battery separators
- •Tubular positive plate batteries requiring high cycle life
Related Products
GT 1000
Self-Crosslinking Binder for Tubular Battery Gauntlets
White Magic GT-1000 is a self-crosslinked acrylic copolymer emulsion engineered for polyester tubular gauntlet fabric used in lead-acid battery separators. It delivers superior thermal and mechanical stability, prevents active material shedding during charge and discharge cycles, and maintains optimal electrolyte permeability.
TB 5000
High Solids Binder for Tubular Battery Gauntlets
White Magic TB-5000 is a self-crosslinked acrylic copolymer emulsion engineered for polyester tubular gauntlet fabric used in lead-acid battery separators. It is the higher-solids variant of GT-1000, formulated for applications requiring heavier fabric build-up in a single impregnation pass.
A 99
Acrylic Battery Gauntlet Impregnation Binder
White Magic A-99 is a self-crosslinked acrylic copolymer emulsion engineered for polyester tubular gauntlet fabric used in lead-acid battery separators. It is formulated as a direct performance equivalent to leading imported battery gauntlet binders.